ACM Rubber - CGPA5821 Series

Name: ACM Rubber - CGPA5821 Series
Brand: CHENGDU FLUORINCHEM NEW MATERIAL CO., LTD.

ACM CGPA5821 is a carboxyl type acrylate rubber, which is formed by emulsion polymer-ization of acrylate monomer and carboxylic acid monomer. It has excellent aging resistance, oil resistance, high temperature resistance and ozone resistance. The Tg of CGPA582D and CGPA5821TR are -28°C and -29°C. It is a low compression set product, and suitable for making rubber hoses, molded products, etc., which is widely used in automobiles, motorcycles, ships, electric power and other fields.

Get A Quote

Category: ACM Rubber

CGPA5821D Specification

Product		ACM		Grade	CGPA5821D		Type	Carboxylic
Test Item					Unit	Standard Value	Test Value	Test Standard
Mooney Viscosity ML(1+4) 100°C					/	37±5	37.7	GB/T 33428-2016
Ash Content					%	≤ 0.60	0.10	GB/T 4498.1-2009
Volatile Content					%	≤ 0.50	0.18	GB/T 24131-2009
Hardness Shore A					Point	63±5	64	ASTM D2240
Tensile Strength					Mpa	≥ 9.00	9.88	ASTM D412
Elongation					%	≥ 250	303	ASTM D412
Compression Set (150°C*72h, 25%)					%	/	31	ASTM D395 (Type2)
Brittle Temperature					°C	/	-24	ASTM D2137
Vulcanization Performance			T10		s	/	49	ASTM D5289
			Ts2		s	/	175
			T90		s	/	460
Thermal Aging (175°C*72h)			Hardness Change		Point	/	-1	ASTM D573
			Tensile Strength Change		%	/	-17.33
			Elongation Change		%	/	12.00
Oil Resistance ASTM3#			Hardness Change		Point	/	-13	ASTM D471
			Tensile Strength Change		%	/	-12.38
			Elongation Change		%	/	6.64
			Volume Change		%	/	16.10
Test Condition	1st Stage		(180°C*10min)		Result		Qualified
	2nd Stage		(175°C*4h)
Shelf Life			2 years
Remark			1.Test Environment: Temperature: 23°C±2°C; humidity: 50%±5%
			2.Test formula: ACM:100 parts; stearic acid:1 part; antioxidant 445:2 parts; microcrystalline wax: 1 part; flow aid FG200: 2 parts; 18D: 0.5 part; Cabot N550: 60 parts; RS735: 3 parts; 1#curing agent: 0.6 part; DOTG-75: 2 parts.

CGPA5821TR Specification

Product		ACM		Grade	CGPA5821TR		Type	Carboxylic
Test Item					Unit	Standard Value	Test Value	Test Standard
Mooney Viscosity ML(1+4) 100°C					/	42±5	42.1	GB/T 33428-2016
Ash Content					%	≤ 0.60	0.01	GB/T 4498.1-2013
Volatile Content					%	≤ 0.50	0.12	GB/T 24131-2009
Hardness Shore A					Point	65±5	64	ASTM D2240
Tensile Strength					Mpa	≥ 10.0	10.5	ASTM D412
Elongation					%	≥ 240	251	ASTM D412
Compression Set (150°C*72h, 25%)					%	/	32	ASTM D395 (Type2)
Brittle Temperature					°C	/	-25	ASTM D2137
Vulcanization Performance			T10		s	/	46	ASTM D5289
			Ts2		s	/	158
			T90		s	/	452
Thermal Aging (175°C*72h)			Hardness Change		Point	/	1	ASTM D573
			Tensile Strength Change		%	/	-19.97
			Elongation Change		%	/	1.02
Oil Resistance ASTM3#			Hardness Change		Point	/	-13	ASTM D471
			Tensile Strength Change		%	/	-11.67
			Elongation Change		%	/	-1.20
			Volume Change		%	/	15.38
Test Condition	1st Stage		(180°C*10min)		Result		Qualified
	2nd Stage		(175°C*4h)
Shelf Life			Two years
Remark			1.Test Environment: Temperature: 23°C±2°C; humidity: 50%±5%
			2.Test formula: ACM:100 parts; stearic acid:1 part; antioxidant 445:2 parts; microcrystalline wax: 1 part; flow aid FG200: 2 parts; 18D: 0.5 part; Cabot N550: 60 parts; RS735: 3 parts; 1#curing agent: 0.6 part; DOTG-75: 2 parts.

Related ACM Rubber